CAR REFINISH PAINT PRIMER EPOXY

Products Inquiry
Click Refresh Verification Code

Description

PRODUCTS DETAILS:


Epoxy Primer

Characteristic: Good fallibility, easy sanding, give excellent rust proofing for bare metal, 

good adhesion power to steel, aluminum, galvanized steel and stainless steel, excellent chemical corrosion resistance and rust resistance.







Substrates

Dried and sanded existing finishes, steel, aluminum, stainless steel, galvanized steel, glass fiber reinforced plastic.

Surface Cleaning

Wash by warm soap, remove wax, silicon and other contaminations with degreaser, sanding with P800-P1000, wash with clean water then keep dry; again with degreaser.

Mixing Ratio

Epoxy Primer

Hardener

Thinner

4

1

1-2

30°C

Epoxy Primer

Epoxy Hardener

Epoxy Thinner

Spray Viscosity

16-19s to drop off, in 4# viscosity cup at 25°C,

Pot-life

At 20°C, 3 hours with hardener.

Re- Treatment

Sanded with P600 or P800 sand paper, do following construction after drying

Spray Gun Set Up

Gravity Feed:  1.2-1.5mm   4-5kg/cm2

Suction Feed:  1.4-1.6mm   4-5kg/cm2

Spray Technology

Coats & Thickness: 2-3 coats, total 25-35um.

Flash-Off Time: At 25°C, 5-10 minutes between two coats, it depends on temperature and paint film.

Drying Time

A. Allow 10-20 minutes air-drying, then 60°C baking 30 minutes, can sand after cool down.

B. Air-drying time 3 hours, at 20°C.

Shelf Life

2 years in original sealed can, cool and dry place at 25°C.

Package

1L×12 or 3.75L×4

























Note:

1. The substrate must be cleaned and sanded before spray, wet sanding P800-1000 and then dry.

2. At ambient temperature higher than 30°C, add appropriate Retarder Solvent into thinner to avoid blushing. 

   For more details, please refer to technical data sheet of Retarder Solvent.

3. The products mixed with hardener should be used up soon and can not be restore for future use; clean equipment immediately with thinner after application,

   otherwise it is very difficult to be cleaned after dry.

FACTORY:


LOADING: